DENILEN B 4010 CB WT
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Vamp Tech |
| Trademark: | DENILEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F1Dt9X_DENILEN-B-4010-CB-WT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP, 40% glass fiber reinforced, not Flame Retardant compound, very good mechanical properties, chemically bonded, thermostabilized, GWFI 650/1-2 GWIT 775/1-2. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.70 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648A |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 1 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 2.00 mm) | 675 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SARANEX™ 553 | The Dow Chemical Company | PVDC | SARANEX™ |
| SCHULABLEND® (PC/ABS) M/MB 5 GF 20 | A. Schulman Europe | PC+ABS | SCHULABLEND® |
| WACKER® Catalyst T 77 | Wacker Chemie AG | Silicone | WACKER® |
| Braskem PP TI4040WT | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Hifax TYS1148PC | LyondellBasell Industries | TPO (POE) | Hifax |