LNP™ LUBRICOMP™ LCL33E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F0Rgy1_LNP-LUBRICOMP-LCL33E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound LCL-4033 EM Product reorder name: LCL33E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.40 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16600 | MPa | ASTM D638 |
| -- | 14700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 180 | MPa | ASTM D638 |
| Break | 187 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.7 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 13000 | MPa | ASTM D790 |
| -- | 14700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 267 | MPa | ASTM D790 |
| -- | 276 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.35 | ||
| vs. Itself - Static | 0.28 | ||
| Wear Factor - Washer | 13.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 3 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 8.80 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | > 299 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | > 240 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.2E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxiglas® MG515 | Maxiglas Corporation | Acrylic (PMMA) | Maxiglas® |
| Boda BDF-LG2752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Elastron® D D400.D35.B | Elastron USA, Inc. | SBS | Elastron® D |
| Karina BLACK PVC COMPOUND 710-48/1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ OC006 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |