Menzolit® AdvancedSMC 0400 Datasheet,Polyester, TS,Menzolit Ltd (UK)-SHANGHAI SUSHENG

Message
Menzolit® AdvancedSMC 0400 is a special low profile SMC for applications within the automotive industry. It satisfies the surface quality needed for automotive body panels. It complies with all automotive regulations, C-Emissions are minimized. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. The temperature resistance of AdvancedSMC allows online painting at standard bake temperatures. The product shows very good adhesion to paint or In Mould Coating (IMC). Because of its zero shrink properties, warpage is eliminated and parts reproducing the dimensions of the cold mould can be produced. Figures given apply to a quasi isotropic 6-layer [0/90/45/-45/90/0] design, different layer designs are possible, please contact our R&D departement. Please check storage conditions printed on packaging label.

General Information
Filler / Reinforcement	Mineral filler Carbon fiber reinforced material
Features	Good dimensional stability Low warpage Low smoke Sprayable Good adhesion Low shrinkage Halogen-free Excellent appearance
Uses	Application in Automobile Field
Forms	Particle
Part Marking Code (ISO 11469)	>UP-(CF+MD)73

Physical	Nominal Value	Unit	Test Method
Density	1.67	g/cm³	ISO 1183
Molding Shrinkage (0°C)	-0.012	%	ISO 294-4
Water Absorption (Saturation, 23°C)	1.0	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus			ISO 527-2
0°C, compression molding	32000	MPa	ISO 527-2
90°C, compression molding	32000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Yield, 0°C, compression molding	200	MPa	ISO 527-2
Yield, 90°C, compression molding	200	MPa	ISO 527-2
Tensile Strain			ISO 527-2
Fracture, 0°C, compression molding	1.4	%	ISO 527-2
Fracture, 90°C, compression molding	2.0	%	ISO 527-2
Flexural Modulus			ISO 178
0°C, compression molding	40000	MPa	ISO 178
90°C, compression molding	20000	MPa	ISO 178
Flexural Stress			ISO 178
0°C, compression molding	400	MPa	ISO 178
90°C, compression molding	400	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179
0°C, compression molding	70	kJ/m²	ISO 179
90°C, compression molding	70	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	185	°C	DSC
CLTE - Flow			ISO 11359-2
0°C	1.7E-6	cm/cm/°C	ISO 11359-2
90°C	1.7E-6	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (2.00 mm)	HB		UL 94

Additional Information
Post Moulding Shrinkage, DIN 53464: 0%Heat Distortion Temperature, EN ISO 75-2: >200°CContinuous Service Temperature, Menzolit Method: 180°CFiber Content UD, total, EN ISO 1172, 90°C: 38%Fiber Content UD, total, EN ISO 1172, 0°C: 54%Poison's Ratio, Menzolit Method, 0°C: 0.3Poison's Ratio, Menzolit Method, 90°C: 0.3Matrix Crazing Strain, Menzolit Method: 0.5%Compression Strength, EN ISO 14126, 0°C: 200 MPaThe value listed as Glass Transition Temp DSC, was tested in accordance with ISO 11357-2.The values listed as Flexural Strength and Lfexural Modulus, ISO 178, were tested in accordance with EN ISO 14125

Additional Information

Post Moulding Shrinkage, DIN 53464: 0%Heat Distortion Temperature, EN ISO 75-2: >200°CContinuous Service Temperature, Menzolit Method: 180°CFiber Content UD, total, EN ISO 1172, 90°C: 38%Fiber Content UD, total, EN ISO 1172, 0°C: 54%Poison's Ratio, Menzolit Method, 0°C: 0.3Poison's Ratio, Menzolit Method, 90°C: 0.3Matrix Crazing Strain, Menzolit Method: 0.5%Compression Strength, EN ISO 14126, 0°C: 200 MPaThe value listed as Glass Transition Temp DSC, was tested in accordance with ISO 11357-2.The values listed as Flexural Strength and Lfexural Modulus, ISO 178, were tested in accordance with EN ISO 14125

Injection	Nominal Value	Unit
Mold Temperature	155 - 160	°C
Injection Pressure	10.0 - 16.0	MPa

Category:	Polyester, TS , Thermoset Polyester
Manufacturer:	Menzolit Ltd (UK)
Trademark:	Menzolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	F05HCX_Menzolit-AdvancedSMC-0400.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 199 X 116346	RTP Company	PP, Unspecified	RTP
Shandong PA1012 GYBMVN	Shandong Guangyin New Materials Co., Ltd.	Nylon 1012	Shandong PA1012
Topilene® J440F	Hyosung Corporation	PP Impact Copolymer	Topilene®
Ad-Tech Epoxy AC-800 A/B	Ad-Tech Plastic Systems Corp.	Epoxy	Ad-Tech Epoxy
KumhoSunny ABS BM530	Shanghai KumhoSunny Plastics Co., Ltd.	ABS	KumhoSunny ABS