Therma-Tech™ TT6600-5001 EC Grey
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Therma-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eyxf76_Therma-Tech-TT6600-5001-EC-Grey.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 14700 | MPa | ISO 527 |
| Tensile Strength 2(Break, 23°C) | 65.0 | MPa | ISO 527 |
| Tensile Elongation 3(Break, 23°C) | 0.50 to 0.80 | % | ISO 527 |
| Flexural Modulus 4(23°C) | 13000 | MPa | ISO 178 |
| Flexural Strength 5(23°C) | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 7.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| Thermal Conductivity | |||
| 23°C 6 | 2.3 to 2.7 | W/m/K | |
| -- 7 | 4.5 to 5.5 | W/m/K | ASTM E1461 |
| -- 8 | 19 to 21 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.00 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 1.50 mm | 925 | °C | |
| 3.00 mm | 925 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 80.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 1.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 10 mm/min |
| 5 . | 10 mm/min |
| 6 . | Through Plane with Modified Transient Plane Source, C-Therm TCi™ |
| 7 . | Through Plane |
| 8 . | In Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6785 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| DELPET™ 80NB | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| DIC.PPS FZ-928N Black | DIC Corporation | PPS | DIC.PPS |
| DINALON® A1X25 MI | Grupo Repol | Nylon 66 | DINALON® |
| Plaskon SMT-B-1 | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |