| Polypropylene homopolymer black with 40% glass fiber, ideal for injection molding, resistant to oil, grease and many solvents, has a high tensile strength and higher HDT, and excellent dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 to 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.35 to 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.040 to 0.080 | % | ASTM D570 |
| Ash Content | 38 to 42 | % | ASTM D2584 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | 100 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7800 | MPa | ASTM D638 |
| Tensile Strength | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5400 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Unannealed | 155 | °C | |
| 1.8 MPa, Unannealed | 130 | °C | |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ASTM D1525 2 |
| -- | 145 | °C | ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 42 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2°C/min |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 10 TFE 15 | RTP Company | Nylon 66 | RTP |
| RTP 140 Z | RTP Company | PP Homopolymer | RTP |
| Geon™ Vinyl Flexible 90215 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina WHITE PVC COMPOUND 805-10/127-A-ERYB-AS-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PIVINEL™ JYY-HARD2 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |