ACRYLITE® M30

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	EvmKDs_ACRYLITE-M30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® M30 acrylic polymer is an amorphous thermoplastic molding compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® acrylic polymers are:

excellent weather resistance

high light transmission

high mechanical strength

high surface hardness and mar resistance

good melt flow rate

versatile colorability due to crystal clarity

The special properties of ACRYLITE M30 polymer are:

medium heat resistance

high melt flow rate

UV light transmitting

medium levels of lubricant

Application:
Used for injection molding optical and technical parts.

General Information
Additive	Lubricant
Features	Amorphous Good Colorability Good Flow Good Weather Resistance High Clarity High Hardness High Strength Lubricated Medium Heat Resistance Scratch Resistant
Uses	Decorative Displays Engineering Parts Lenses Lighting Applications Medical/Healthcare Applications Optical Applications Piping
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.19	g/cm³	ASTM D792
Apparent Density	0.66	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	24	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.60	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	89		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3240	MPa	ASTM D638
Tensile Strength	63.4	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	2.0 to 4.0	%
Break	2.0 to 4.0	%
Flexural Modulus	3170	MPa	ASTM D790
Flexural Strength	107	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 6.35 mm)	19	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	82.2	°C	ASTM D648
Vicat Softening Temperature	90.0	°C	ASTM D1525
CLTE - Flow (0 to 156°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	92.0	%	ASTM D1003
Haze (3200 µm)	< 1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	< 1.0	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
RTP 301 FR	RTP Company	PC	RTP
VAMPLEN 1025 V2	Vamp Tech	PP Homopolymer	VAMPLEN
Hostacom LPX 1702 100015	LyondellBasell Industries	PP Copolymer	Hostacom
INEOS PP N02J-00	INEOS Olefins & Polymers USA	PP Impact Copolymer	INEOS PP
Kafrit PEX TA 2613 CL	Kafrit NA Ltd.	XLPE	Kafrit PEX