| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EvHeux_AKROLOY-PA-ICF-40-black-5270-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA ICF 40 black (5270) is a 40% carbon fibre reinforced polyamide blend with high stiffness, good sliding properties and reduced moisture. Application areas are mechanically high stressed parts with dimensional stability and moisture independent properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 15.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 30.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.42 | -- | % | |
| Flow | 0.28 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.3 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 1.5 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 40 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 35000 | 32000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | 230 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 35000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 400 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 8.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | -- | kJ/m² | |
| 23°C | 50 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 255 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+4 | 1.0E+4 | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-3450 | Quantum Composites Inc. | TS, Unspecified | Quantum Composites |
| Tecoform® PO30 GB30 NL HS | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| Sunny® PA66 EB300 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| Alpha PVC GW 3026 NAT.LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Sylvin 4250-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |