Generic Nylon 6 - Unspecified
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EuwMxO_Generic-Nylon-6---Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Unspecified This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.22 - 3.04 | g/cm³ | ASTM D792 |
| 23°C | 1.18 - 2.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 1.2 | % | ASTM D955 |
| 23°C | 0.27 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.10 - 1.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.80 - 2.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1900 - 11500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 44.8 - 81.9 | MPa | ASTM D638 |
| Fracture, 23°C | 78.3 - 122 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.0 - 3.6 | % | ASTM D638 |
| Fracture, 23°C | 0.50 - 3.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4340 - 8390 | MPa | ASTM D790 |
| 23°C | 6150 - 14700 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 48.3 - 193 | MPa | ASTM D790 |
| 23°C | 65.0 - 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 - 41 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 41 - 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 122 - 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 - 201 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.1E+2 - 2.5E+12 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 51 - 5.1E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 95.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 250 - 283 | °C | |
| Mold Temperature | 60.0 - 92.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 HF NTLA010 PR306 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| HiFill® PA6 GF35 LE | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Huafon JF-HSY-9510 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Moplen HP6057 | LyondellBasell Industries | PP Homopolymer | Moplen |
| NORYL™ GFN1 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |