MonoSol® M8630 - 3 mil
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EuqYEo_MonoSol-M8630---3-mil.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol M8630 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology. MonoSol M8630 film has been specially formulated to be completely resistant to alkaline hydrolysisup to 14 pH. Coupling its rapid cold water solubility and compatibility to alkaline compounds, M8630 film is an excellent candidate for Detergent and Disinfectant unit dose packaging. It has good cold crack resistance and can be easily converted on all conventional packaging machines. Standard thicknesses are 25 micron (1.0 mil), 38 micron (1.5 mil), 51 micron (2.0 mil) and 76 micron (3.0 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 8.3 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 76.2 µm | 33.0 | sec | |
| Dissolution : 10°C, 76.2 µm | 56.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (76.2 µm) | 9.96 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 76 | µm | |
| Film Thickness - Recommended / Available | 25 µm, 38 µm, 51 µm, and 76 µm | ||
| Secant Modulus - 100%, MD | 10.3 | MPa | ASTM D882, ISO 527-3 |
| Tensile Strength - MD | |||
| Break | 37.2 | MPa | ASTM D882 |
| -- | 37.2 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Break) | 590 | % | ASTM D882, ISO 527-3 |
| Dart Drop Impact | 2200 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength - MD | |||
| -- | 940 | g | ASTM D1922 |
| -- | 0.096 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP600V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Next Nylon 66 Prime Series PXR-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| AFFINITY™ KC 8852G | The Dow Chemical Company | POP | AFFINITY™ |
| HIDEN® U090 L | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE, UHMW | HIDEN® |
| ISOTHANE® 1180A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |