Vyncolit® E 8833C
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EtV6Ou_Vyncolit-E-8833C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E8833C is a fiberglass reinforced epoxy molding compound, with excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.89 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 85.0 | MPa | ASTM D638 |
| Flexural Modulus | 18000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 140 | MPa | ASTM D790 |
| Compressive Strength | 200 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| CLTE - Flow | 3.7E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.35 mm) | V-1 | UL 94 |
| Additional Information |
|---|
| The value listed as CTLE Flow, ASTM D696, was tested in accordance with ASTM D3386.Powder Density, ASTM D1895: 0.9 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 0.2%Dielectric Strength, ASTM D149, 60 Hz, Method B, wet: 13 kV/mmDielectric Constant, ASTM D150, 1000000 Hz, wet: 4Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.02 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVP™ GYYHSUVCP | SABIC Innovative Plastics | Nylon 66 | AVP™ |
| DOMAMID® 66ST1 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Formolon® 265 | Formosa Plastics Corporation, U.S.A. | PVC Alloy | Formolon® |
| Karina BLACK PVC COMPOUND -E TR-652D48/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF00CSXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |