HiFill® HDPE GF15 50100
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Es24dO_HiFill-HDPE-GF15-50100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® HDPE GF15 50100 is a High Density Polyethylene product filled with 15% glass fiber. It can be processed by extrusion and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4070 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 129 | °C | |
| 1.8 MPa, Unannealed | 121 | °C | |
| CLTE - Flow | 5.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 12 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 232 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 218 to 246 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P1187 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sylvin 2905-85 Black 289 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Grilamid® 2SV-30H black 9992 | EMS-GRIVORY | Nylon 610 | Grilamid® |
| Epolene® C-17P | Westlake Chemical Corporation | LDPE | Epolene® |
| ESTOPLAST EP 4030GY99 | Ester Industries Ltd. | PBT | ESTOPLAST EP |