Ingeo™ 8052D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eqi2yX_Ingeo-8052D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ingeo 8052D - a product from NatureWorks LLC - can be converted into an expanded foam sheet with use temperatures up to 77°F (25°C). This foam is lightweight, strong and suitable for packaging fresh meat and vegetables. In order to extrude foam with the desired expansion properties, this grade must be modified with a branching agent such as Joncryl® 4368C. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | |
| Relative Viscosity | 3.30 | Internal method |
| Optical | Nominal Value | ||
|---|---|---|---|
| Clarity | Transparent |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 3550 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 - 65.0 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 145 - 160 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 5.0E-3 | % | |
| Hopper Temperature | 21.1 | °C | |
| Cylinder Zone 1 Temp. | 166 | °C | |
| Cylinder Zone 2 Temp. | 193 | °C | |
| Cylinder Zone 3 Temp. | 204 | °C | |
| Adapter Temperature | 204 | °C | |
| Melt Temperature | 199 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa |
| Extrusion instructions |
|---|
| Screw Speed: 100 to175 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 HT 7500 GF 40 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Adell PBT HR-34 | Adell Plastics, Inc. | PBT | Adell PBT |
| CALP GF3010A | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Karina WHITE PVC COMPOUND -E 839-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 350-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |