PolyFibra® PF-PEI02
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | FuturaMat |
| Trademark: | PolyFibra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EoqFwp_PolyFibra-PF-PEI02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PF-PEI02 is an agromaterial descending from the PolyFibra range. PF-PEI02 is a Polypropylene strongly reinforced by wood fibers (spruce). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 to 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 to 1.7 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 66 to 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2640 to 3640 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 27.0 to 45.0 | MPa | |
| Break | 27.0 to 45.0 | MPa | |
| Tensile Strain (Yield) | 2.0 to 3.4 | % | ISO 527-2 |
| Flexural Modulus | 3250 to 5090 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 10 to 18 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 79.0 to 87.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® HHM TR-258 | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| POLYLAN AG15A1 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Anjaconduct® 350-KF1E3 | Almaak International GmbH | Nylon 66 | Anjaconduct® |
| Exxelor™ VA 1801 | ExxonMobil Chemical | TP, Unspecified | Exxelor™ |
| DURACON® EB-08 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |