K-vinyl 90 Deg C Rating Insulation (88-Wet)
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Technovinyl Polymers India Ltd. |
| Trademark: | K-vinyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EodEdp_K-vinyl-90-Deg-C-Rating-Insulation-88-Wet-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-vinyl 90 Deg C Rating Insulation (88-Wet) is a Polyvinyl Chloride material. It is available in Africa & Middle East. Primary attribute of K-vinyl 90 Deg C Rating Insulation (88-Wet): RoHS Compliant. Typical application of K-vinyl 90 Deg C Rating Insulation (88-Wet): Wire & Cable |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield 1 | 14.9 | MPa | |
| Yield | 14.8 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break 2 | 210 | % | |
| Break | 250 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -19.0 | °C | ASTM D746 |
| Note Message | |
|---|---|
| 1 . | 100°C for 7 days ageing |
| 2 . | 100°C for 7 days ageing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOFORCE® PEEK C2300 | LEIS Polytechnik - polymere Werkstoffe GmbH | PEEK | TRIBOFORCE® |
| New-prene™ 6155B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Gallonprene® GP210-7509 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GAPEX® RPP30EA36HB | Ferro Corporation | PP Homopolymer | GAPEX® |
| HiFill® PA6/6 GF20 HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |