Hostacom X M2 T11 104420
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eo6gmU_Hostacom-X-M2-T11-104420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom X M2 T11 104420 is a 20% mineral filled elastomer modified PP copolymer with high flow, high impact resistance also at low temperature. The product is specially designed for automotive interior trims. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LB03525 - C | Premier Polymers, LLC. | LLDPE | Premier |
| Telcar® TL-2683B | Teknor Apex Company | TPO (POE) | Telcar® |
| Toraycon® 1401X06 | Toray Resin Company | PBT | Toraycon® |
| BJB Polyurethane TC-8740 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| GTPO™ 8001 | S&E Specialty Polymers, LLC | TPO (POE) | GTPO™ |