VYPET VNT 630 FR
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Enzzkv_VYPET-VNT-630-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vypet 630 FR is a 30 % glass reinforced Flame retardant, PET injection molding compound designed for electrical and structural applications. Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 2.00mm | 0.20 | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.90 | % | ASTM D955 |
| Vertical flow direction : 2.00mm | 0.90 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 1 | 145 | MPa | ASTM D638 |
| Fracture | 145 | MPa | ISO 527-2/5 |
| Flexural Modulus 2 | |||
| -- | 10200 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| Flexural Strength 3 | 215 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 90 | J/m | ASTM D256 |
| 23°C | 8.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 228 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 225 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 29 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.30 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.850 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 5VA | UL 94 | |
| 3.00 mm | V-0 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 275 - 295 | °C | |
| Processing (Melt) Temp | 275 - 295 | °C | |
| Mold Temperature | 95.0 - 120 | °C | |
| Injection Pressure | 55.0 - 85.0 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 75 | rpm |
| Injection instructions |
|---|
| Back Pressure: No Back |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AURUM® PL6200 | Mitsui Chemicals, Inc. | PI, TP | AURUM® |
| DESLON™ 6 DSC101IG6 | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| Epoxies, Ect. 20-3068 (CAT.1) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Karina BEIGE PVC COMPUOND -E 500D08/201 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pier One POM AH500P-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |