iMPACT 100®
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | iMPACT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EmlWee_iMPACT-100-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
iMPACT 100® is a black High Density Polyethylene Resin suitable for all dimensions of PE100 piping where transportation of potable water, irrigation, efflluent, slurry and certain chemical substances is required. It is a high molecular mass grade with good impact strength, abrasion, chemical and UV resistance and complies with the PE100 material requirements of ISO 4427:2007 and ISO 4437:2007. iMPACT 100® High Density Polyethylene is supplied only in the form of black UV resistant granules. Typical Applications Pipes for:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.957 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.0 | g/10 min | |
| 190°C/5.0 kg | 0.30 | g/10 min | |
| Carbon Black Content | 2.0 to 2.5 | % | ISO 6964 |
| Carbon Black Dispersion | < 3 | ISO 18553 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | > 20 | min | ISO 11357 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, Compression Molded | 26.0 | MPa | |
| Break, Compression Molded | 33.0 | MPa | |
| Tensile Elongation 3(Break, Compression Molded) | > 760 | % | ASTM D638 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 160 to 170 | °C | |
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 2 Temp. | 190 to 220 | °C | |
| Cylinder Zone 3 Temp. | 190 to 220 | °C | |
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF5THT (Series: FC/ht) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Mylar® MO 21 (1400 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Argothane® 19424 | Argotec LLC | TPU, Unspecified | Argothane® |
| Catalyst PS/2LR | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| INEOS HDPE K54-05 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |