Reslen PPH 40T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polimarky Spolka Jawna |
| Trademark: | Reslen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ElumaP_Reslen-PPH-40T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reslen PPH 40T is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in Europe. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 to 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 20 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 to 2600 | MPa | ISO 527-2 |
| Tensile Stress | 20.0 to 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 to 80 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 to 5.0 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 67.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 158 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAKEEP® Care M40G | Evonik Industries AG | PEEK | VESTAKEEP® Care |
| KRATON® G1650 M | Kraton Polymers LLC | SEBS | KRATON® |
| KumhoSunny PC 2502NH | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| INEOS LLDPE LL6910KJ | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| Karina GRAY PVC COMPOUND 800-18/233-A-ERYB (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |