Devcon Plastic Steel Putty (A)
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ElCdDt_Devcon-Plastic-Steel-Putty-A-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A steel-filled epoxy putty that cures at room temperature and is designed for filling, rebuilding, and bonding metal surfaces. Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.33 | g/cm³ | |
| Specific Volume | 0.430 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 121 | °C | |
| Wet | 49 | °C | |
| Tensile Shear Adhesion | 19.3 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.060 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5860 | MPa | ASTM D638 |
| Flexural Strength | 38.6 | MPa | ASTM D790 |
| Compressive Strength | 57.0 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.57 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 1.2 | kV/mm | ASTM D149 |
| Dielectric Constant | 67.5 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 9.0 Mixing ratio by capacity: 2.5 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 45 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GF 15 1 L black (4673) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Altuglas® VSE UVT | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Fiberfil® J-60/20/FR | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| LEXAN™ XHT1141 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ LUBRICOMP™ 5CL23 compound | SABIC Innovative Plastics | PVDF | LNP™ LUBRICOMP™ |