AvaSpire® AV-650 GF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eiyqcy_AvaSpire-AV-650-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AvaSpire® AV-650 GF30 is a 30% glass fiber-reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide a high degree of chemical resistance and higher mechanical strength and stiffness than unfilled AV-650 resin. This material can be repeatedly exposed to harsh chemicals and prolonged steam sterilization cycles without any significant loss of properties. Potential applications for this resin include orthopedic and dental instruments, surgical power tool battery housings and other devices and components requiring a combination of high temperature performance and high environmental resistance. AvaSpire® AV-650 GF30 can be easily processed by typical injection molding and extrusion methods using standard equipment.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.18 mm | 0.80 to 1.0 | % | |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Water Absorption - 30 days | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 10100 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 165 | MPa | ISO 527-2/1A/5 |
| -- | 142 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 9000 | MPa | ASTM D790 |
| -- | 9800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 221 | MPa | ASTM D790 |
| -- | 240 | MPa | ISO 178 |
| Compressive Strength | 163 | MPa | ASTM D695 |
| Shear Strength | 80.8 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 96 | J/m | ASTM D256 |
| -- | 13 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 960 | J/m | ASTM D4812 |
| -- | 69 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 4(1.8 MPa, Annealed, 3.20 mm) | 209 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | ASTM D3418 |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 1.9E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1290 | J/kg/°C | |
| 200°C | 1670 | J/kg/°C | |
| Thermal Conductivity | 0.29 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.00 mm) | 14 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.65 | ||
| 1 kHz | 3.66 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 2.0E-3 | ||
| 1 kHz | 0.0 | ||
| 1 MHz | 5.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 410 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 365 | °C | |
| Middle Temperature | 370 | °C | |
| Front Temperature | 375 | °C | |
| Nozzle Temperature | 380 | °C | |
| Processing (Melt) Temp | 365 to 390 | °C | |
| Mold Temperature | 150 to 180 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 2 hours at 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AA36NT6503 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| EMOPLEN® A 1102 T4 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Kepital® F10-01 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Iupiace® LN23 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Sylvin 8200-70 Brown 7412 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |