Generic Ionomer
| Category: | Ionomer , Ionomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eiol6G_Generic-Ionomer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Ionomer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.938 - 0.971 | g/cm³ | ASTM D792 |
| 23°C | 0.940 - 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.65 - 14 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.80 - 14 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 60 - 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 13.0 - 45.0 | MPa | ASTM D638 |
| Fracture, 23°C | 10.3 - 33.1 | MPa | ASTM D638 |
| Fracture, 23°C | 21.8 - 22.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 400 - 410 | % | ASTM D638 |
| Fracture, 23°C | 400 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 207 - 761 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 33.6 - 38.6 | MPa | ASTM D882 |
| TD : Fracture | 26.5 - 40.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 250 - 350 | % | ASTM D882 |
| TD : Fracture | 250 - 410 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 59.5 - 81.3 | °C | ASTM D1525 |
| -- | 59.5 - 79.0 | °C | ISO 306 |
| Peak Melting Temperature | 86.3 - 101 | °C | ASTM D3418, ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 2.7 - 4.2 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 264 | °C | |
| Mold Temperature | 26.7 - 38.3 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic IonomerThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 - 160 | °C | |
| Cylinder Zone 2 Temp. | 160 - 210 | °C | |
| Cylinder Zone 3 Temp. | 185 - 236 | °C | |
| Cylinder Zone 4 Temp. | 185 - 236 | °C | |
| Cylinder Zone 5 Temp. | 185 - 236 | °C | |
| Adapter Temperature | 185 - 235 | °C | |
| Melt Temperature | 198 - 237 | °C | |
| Die Temperature | 185 - 236 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic IonomerThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MOSTEN EH 801 | UNIPETROL RPA | PP Random Copolymer | MOSTEN |
| TRAMID® 4110G20 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Lotrène® LLDPE Q2018H | QATOFIN Company Limited | LLDPE | Lotrène® LLDPE |
| Hostacom T20C557 3211 | LyondellBasell Industries | PP Copolymer | Hostacom |
| FUDOWLITE® F5637 | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |