| Message |
|---|
| TEM 9053C is a short fiberglass reinforced, toughened epoxy molding compound, with excellent dimensional stability, high strength properties and good electrical insulation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.92 | g/cm³ | ASTM D792 |
| Apparent Density | 0.85 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.25 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 100 | MPa | ASTM D638 |
| Flexural Modulus | 16600 | MPa | ASTM D790 |
| Flexural Strength (Break) | 160 | MPa | ASTM D790 |
| Compressive Strength | 235 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 160 | °C | ASTM D648 |
| CLTE - Flow | 2.6E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.71 | W/m/K | ASTM C518 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 16 | kV/mm | |
| -- 3 | 14 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 4.20 | ASTM D150 | |
| Dissipation Factor 5(1 MHz) | 0.015 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | 60 Hz, Wet |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LC 145 | A. Schulman Europe | ABS | POLYMAN® |
| RTP 2300.5 C | RTP Company | TPU-Polyester | RTP |
| BITONER® BT-1200H | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| APEX® 3800-70NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ THERMOTUF™ VF008 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |