Veradel® A-702
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Veradel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ei2bAS_Veradel-A-702.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Veradel® polyethersulfone (PESU) is transparent and offers high heat deflection temperatures, excellent toughness and dimensional stability, and resistance to steam, boiling water and mineral acids. Other desirable properties include thermal stability, creep resistance and inherent flame resistance. Veradel® A-702 is a very high melt flow grade suggested for compounding, especially of glass or carbon fiber reinforced compounds. This grade was formerly marketed as Radel® A PESU
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 75 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Water Absorption - 30 days | 1.9 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D638 |
| Tensile Strength | 88.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648 |
| CLTE - Flow | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.51 | ||
| 1 kHz | 3.50 | ||
| 1 MHz | 3.54 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.7E-3 | ||
| 1 kHz | 2.2E-3 | ||
| 1 MHz | 5.6E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 2.5 | hr | |
| Processing (Melt) Temp | 343 to 385 | °C | |
| Mold Temperature | 149 to 163 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.2:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 2.5 | hr | |
| Cylinder Zone 1 Temp. | 335 to 391 | °C | |
| Cylinder Zone 2 Temp. | 335 to 391 | °C | |
| Cylinder Zone 3 Temp. | 335 to 391 | °C | |
| Cylinder Zone 4 Temp. | 335 to 391 | °C | |
| Cylinder Zone 5 Temp. | 335 to 391 | °C | |
| Adapter Temperature | 327 to 371 | °C | |
| Melt Temperature | 343 to 391 | °C | |
| Die Temperature | 327 to 371 | °C |
| Note Message | |
|---|---|
| 1 . | These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201A GB 20 | RTP Company | Nylon 6 | RTP |
| Sinvicomp SRF9703 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| UMG ABS® GF10 | UMG ABS, Ltd. | ABS | UMG ABS® |
| ALAMID® 6 HZ 4 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | ALAMID® |
| Geon™ Vinyl Rigid Extrusion L7100 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |