OmniLon™ PA6/6 GR43
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eg7IDD_OmniLon-PA6-6-GR43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 43% Glass Reinforced, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 197 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 13100 | MPa | ASTM D790 |
| Flexural Strength | 296 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 260 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 249 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEV-4335M70 | SHIN-A T&C | Epoxy | SHIN-A |
| Flontech® FT-PPS15-CARR10-M2-2 | Guarniflon S.p.A. - Flontech Division | PTFE+PPS | Flontech® |
| EnDura® V91A | Precision Polymer Engineering Ltd. | Fluorelastomer | EnDura® |
| Leona™ 1502 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LUVOCOM® TPU-7682 | Lehmann & Voss & Co. | PUR, Unspecified | LUVOCOM® |