MARPOL® HDP 580
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Efxraf_MARPOL-HDP-580.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MARPOL® HDP 580 is a high performance copolymer that is designed for the most demanding requirements of pressure pipe applications. It has good long-term hoop strength performance, very high melt strength, and outstanding toughness even at low temperatures. Recommended Applications: Containers for potable water, oil, and gas. Distribution and gathering; chemical, industrial, mining, and sewer. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.944 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | |
| 190°C/21.6 kg | 8.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.1 | MPa | |
| Break | 34.5 | MPa | |
| Tensile Elongation 1(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 758 | MPa | ASTM D3350 |
| -- | 965 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® PR40 | Nilit Plastics | Nylon 66 | POLYNIL® |
| PRL PC-FR2A-D | Polymer Resources Ltd. | PC | PRL |
| Dynaflex™ D3204-1000-03 | PolyOne Corporation | TPE | Dynaflex™ |
| Elastocon® SMR1000 | Elastocon TPE Technologies | TPO (POE) | Elastocon® |
| I. Stern 750 | I. STERN & CO. INC. | ABS | I. Stern |