EUROPLEX® Film HC 0F052
| Category: | PVDF+PMMA , Polyvinylidene Fluoride + Acrylic (PMMA) |
| Manufacturer: | Evonik Industries AG |
| Trademark: | EUROPLEX® Film |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EeN56q_EUROPLEX-Film-HC-0F052.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EUROPLEX® Film HC 0F052 is a weather resistant, transparent and optical quality co-extruded PMMA and PVDF film for graphic lamination systems. This film displays excellent performance in long term outdoor weathering without experiencing color change or yellowing. EUROPLEX® Film HC 0F052 provides high protection for other polymeric substrates against degradation caused by UV radiation. Due to its PVDF top layer, the film displays a very good chemical resistance, anti-soiling and easy to clean effect. Application EUROPLEX® Film HC 0F052 can be laminated as a protective top layer onto polymeric films and sheets based on PVC, ABS, PC, and ASA. Decorative films protected with EUROPLEX® on top can be thermoformed and laminated on different substrates, such as PVC profiles, or used in complex shapes molding processes such as In-Molding Decoration. In labels or Graphic Arts, EUROPLEX® Film HC 0F052 can be used as a high quality clear overlay in laminate systems for high UV and weathering protection. Chemical resistant, anti-soiling and easy to clean effects are achieved. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | DIN 53479 |
| Surface Tension - PVDF side | 23 | mN/m | DIN 53364 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance - 280 - 380 nm | < 0.50 | % | DIN EN 410 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Accelerated Weathering Resistance - method A, cycle 1, 65% RH 1 | No Visible Change | ISO 4892-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| Yield | 7.0 | % | |
| Break | 100 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 92.0 | % | ISO 13468-2 |
| Haze | < 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 15,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3100-20 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| TRANSMARE® 44CB70 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Hifax CB 1160 G1 G74010 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 8367-69 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ZEONEX® K26R | Zeon Corporation | COP | ZEONEX® |