Karina IVORY PVC COMP. -E 105852-35/ 1-A-IS-L
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EbkClD_Karina-IVORY-PVC-COMP--E-105852-35-1-A-IS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PVC COMPOUND RECOMMENDED FOR EXTRUSION OF WIRES THHN AND THWN |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.31 to 1.37 | g/cm³ | IEC 60811-1-3 |
| Color | OK | ME 12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 83 to 87 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 13.8 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 13.8 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | NBR 5403 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 28 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 136°C |
| 3 . | Aged in Air for 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 38F 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Tarnamid® T-27 GF 35 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| COPYLENE® CH200LN | Phillips 66 | PP Homopolymer | COPYLENE® |
| Daploy™ WB135HMS | Borealis AG | PP Homopolymer | Daploy™ |
| Koylene SR20NS | Reliance Industries Limited | PP Random Copolymer | Koylene |