INEOS LLDPE LL6608AF
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EbdugG_INEOS-LLDPE-LL6608AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6608AF has been developed for lean and rich blend blown film applications, such as rigid layers in coextrusion, carrier bags, refuse sacks and liners. This grade is also recommended for artificial grass applications. LL6608AF is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL6608AF. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 290 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, blown film | 14.0 | MPa | ISO 527-3 |
| TD : Yield, 38 µm, blown film | 16.0 | MPa | ISO 527-3 |
| MD : 38 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : 38 µm, blown film | 35.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 38 µm, blown film | 750 | % | ISO 527-3 |
| TD : Broken, 38 µm, blown film | 900 | % | ISO 527-3 |
| Dart Drop Impact (38 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38.0 µm | 43.1 | kN/m | ASTM D1922 |
| TD : 38.0 µm | 255.0 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 116 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 56 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALP 1460G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| CoolPoly® E8103 | Celanese Corporation | TPE | CoolPoly® |
| Fainplast PVC CRKA 90 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| GAPEX® RPP10EB15WH | Ferro Corporation | PP Homopolymer | GAPEX® |
| K-Resin® SBC BK10 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |