ADENE BXQB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A.D. Compound spa |
| Trademark: | ADENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EawrvU_ADENE-BXQB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADENE BXQB is a Polypropylene Homopolymer (PP Homopolymer) material filled with 20% calcium carbonate and 20% talc. It is available in Europe or North America. Primary attribute of ADENE BXQB: Homopolymer. Typical application of ADENE BXQB: Appliances |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Ash Content | 40 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | 12 | % | |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 3748 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Pro-fax RP735S | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| RTV-2 GI-1110 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| BESTNYL SE00VI01AM-1 | Triesa Plastics | Nylon 66 | BESTNYL |
| Innothane® FM-2050 | Innovative Polymers, Inc. | TSU | Innothane® |