TUFLIN™ HS-7028 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | TUFLIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EYPi58_TUFLIN-HS-7028-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene copolymer, linear low density (LLDPE) resin designed for good strength and processability. This product is recommended for general purpose packaging applications from thick gauge, heavy duty bags to high speed thin gauge applications
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | Internal method |
| Film Puncture Energy | 4.52 | J | Internal method |
| Film Puncture Force | 48.9 | N | Internal method |
| Film Puncture Resistance | 24.8 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 82.7 | J/cm³ | ASTM D882 |
| TD | 82.7 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 262 | MPa | ASTM D882 |
| 2% secant, MD | 214 | MPa | ASTM D882 |
| 1% secant, TD | 255 | MPa | ASTM D882 |
| 2% secant, TD | 214 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 12.1 | MPa | ASTM D882 |
| TD : Yield | 11.7 | MPa | ASTM D882 |
| MD : Fracture | 37.9 | MPa | ASTM D882 |
| TD : Fracture | 37.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 500 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Dart Drop Impact | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 380 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 109 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 34 | ASTM D2457 | |
| Haze | 18 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸 (63.5 mm) 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 熔体温度：415 °F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5 比 1 螺杆速度：39 rpm 冷冻线高度：57 英寸 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 84709 | RTP Company | PTT | RTP |
| Stamylex® 2258 | Borealis AG | LDPE | Stamylex® |
| Monprene® OM-10268-01 | Teknor Apex Company | TPE | Monprene® |
| Bergamid™ B700 G20 H UF | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Devcon Titanium Putty | Devcon | Epoxy | Devcon |