BCC Resins BC 8160
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EYO5T1_BCC-Resins-BC-8160.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC8160 is a low viscosity two-component urethane casting compound that is specifically formulated for its flexural and impact strength. It is recommended for use for the production casting of highly wear-resistant parts and prototypes. BC8160 can be used to develop thermoplastics type prototypes. This product is a safe, easy-to-handle, room temperature mixing and curing system that does not contain TDI, MDI, or MOCA. BC8160 is relatively insensitive to typical environmental moisture and will make good void-free parts without the problems that some conventional urethane systems exhibit. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Volume | 0.910 | cm³/g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Life (24°C) | 16.0 to 20.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.25 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 to 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 248 | MPa | ASTM D638 |
| Flexural Modulus | 538 | MPa | ASTM D790 |
| Flexural Strength | 25.5 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | 114 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 60, Mix Ratio by Volume: 60 | ||
| Thermoset Mix Viscosity 1(24°C) | 1400 to 1500 | cP | ASTM D2393 |
| Demold Time (23°C) | 6.0 to 8.0 | min | |
| Post Cure Time | |||
| 23°C | 72 to 120 | hr | |
| 66°C | 16 | hr |
| Note Message | |
|---|---|
| 1 . | Mixed, 1.5 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1004-625UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sylvin 8207-75FU White 1483 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TORZEN® M1500HS GR01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Zhongfa PP FR-08 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| MAJORIS DW464 | AD majoris | PP Copolymer | MAJORIS |