LNP™ LUBRICOMP™ DFL32XXP compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EXV0BO_LNP-LUBRICOMP-DFL32XXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DFL32XXP is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound DFL-4032 Product reorder name: DFL32XXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 74.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3600 | MPa | ISO 178 |
| Flexural Stress | 118 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(-30°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 141 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.3E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Grilamid® TR 90 LS | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Jam PE 18YF5 | Jam Petrochemical Company | LLDPE | Jam PE |
| Karina CLEAR PVC COMPOUND 75/200-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 4261 AG | LyondellBasell Industries | HDPE, HMW | Lupolen |
| Moplen HP420J | PolyMirae | PP Homopolymer | Moplen |