MAXAMID™ PA66 ST801HSL BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EXGo4x_MAXAMID-PA66-ST801HSL-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA66 ST801HSL Nylon 66 impact modified heat stabilized resin for injection molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 180 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1690 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 71.0 | °C | ASTM D648 |
| Peak Melting Temperature | 255 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A70 G50 H Natural | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Geon™ 180 Series 180X5 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 180 Series |
| KumhoSunny PBT/ASA HBA5810M | Shanghai KumhoSunny Plastics Co., Ltd. | PBT+ASA | KumhoSunny PBT/ASA |
| IROGRAN® A 92 E 4670 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ISOTHANE® 1085AF | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |