NORYL™ WCD891B resin
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EX2ZLK_NORYLWCD891Bresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-halogenated flame retardant, flexible NORYL resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use temperature requirements as defined by UL 1581. 89 Shore A hardness. Good processing by using standard extrusion equipment. UL1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 89 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 18.0 | MPa | UL 1581 |
| Fracture 1 | 16.0 | MPa | ASTM D638 |
| Fracture, 113°C 2 | 21.0 | MPa | UL 1581 |
| Fracture | 15.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 140 | % | ISO 527-2/50 |
| Fracture | 220 | % | UL 1581 |
| Fracture 3 | 170 | % | ASTM D638 |
| Fracture, 113°C 4 | 160 | % | UL 1581 |
| Flexural Modulus 5 | |||
| 100mm span | 160 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 7.00 | N/mm | ISO 6383-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| UL Temperature Rating | 80 | °C | UL 1581 |
| Heat Deformation 6(100°C) | 9.0 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| VW-1 | Pass | UL 1581 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.1E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.5E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm, in Oil) | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.00 mm, Testing by SABIC) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 250 | °C | |
| Cylinder Zone 5 Temp. | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 25 - 120 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 220 - 250 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 220 - 250 °CScreen Pack: 150 - 100Screw Speed: 15 - 85 rpmWater Bath Temperature: 15 - 60 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | After 7 days |
| 3 . | Type 1, 50mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SZF6208 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| NEFTEKHIM PP 8548S (EPH71HA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| HAIPLEN H50 G6 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| 3M™ Dyneon™ PTFE Compound TF R4303 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Sylvin 2807-80 White 1437 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |