ELITE™ 5960G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EWg5QS_ELITE-5960G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.962 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 0.339 | J | |
| Film Puncture Force | 13.3 | N | |
| Film Puncture Resistance | 1.41 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 141 | J/cm³ | ASTM D882 |
| TD | 128 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 1120 | MPa | ASTM D882 |
| 2% secant, MD | 876 | MPa | ASTM D882 |
| 1% secant, TD | 1330 | MPa | ASTM D882 |
| 2% secant, TD | 1020 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 28.3 | MPa | ASTM D882 |
| TD : Yield | 30.3 | MPa | ASTM D882 |
| MD : Fracture | 37.2 | MPa | ASTM D882 |
| TD : Fracture | 24.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 500 | % | ASTM D882 |
| TD : Fracture | 600 | % | ASTM D882 |
| Dart Drop Impact | 40 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 13 | g | ASTM D1922 |
| TD | 400 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 134 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 14 | ASTM D2457 | |
| Haze | 42 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film:Screw Size: 3.5 inScrew Type: DSB IIDie Gap: 70 mil (1.7 mm)Melt Temperature: 425°FOutput: 12 lb/hr/in of die circumferenceDie Diameter: 8 in.Blow-Up Ratio: 2.5 to 1Frost Line Height: 33 in. |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycast 612VS C-80 | Cast Nylons Ltd. | Nylon 612 | Nycast |
| Endura® FR-7072-3 | PMC Group Polymer Products | PP Copolymer | EnDura® |
| KOCETAL® TF301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Sylvin 8260-70FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH TPR OTR4595-Soles | OTECH Corporation | TPE | OTECH TPR |