| Nickel-Coated Carbon Fiber - Electrically Conductive - EMI/RFI Shielding - Preliminary Data Sheet |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.050 - 0.20 | % | ASTM D955 |
| Moisture Content | 0.020 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ASTM D638 |
| Tensile Strength | 152 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 - 1.5 | % | ASTM D638 |
| Flexural Modulus | 13800 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 380 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+2 | ohms | ASTM D257 |
| -- | < 10 | ohms | ESD STM11.11 |
| Volume Resistivity | < 0.10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 243 - 274 | °C | |
| Mold Temperature | 51.7 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoFin 1355 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| Electrafil® J-50/CF/30/TF/15 | Techmer Engineered Solutions | PC | Electrafil® |
| Golden Compound PP S²PC 3545 BO 15IM16 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| Karina BLACK PVC COMPOUND 751-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DFL36HL compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |