Hostaform® LM140LGZ
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EWDOLr_Hostaform-LM140LGZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostaform® acetal copolymer grade LM140LGZ is a laser markable specialty grade of acetal copolymer formulated to provide good flow with a low gloss finish and improved UV resistance. Preliminary Data Sheet |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 41.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 175 | °C | |
| Middle Temperature | 170 - 180 | °C | |
| Front Temperature | 175 - 185 | °C | |
| Nozzle Temperature | 185 - 195 | °C | |
| Processing (Melt) Temp | 180 - 195 | °C | |
| Mold Temperature | 80.0 - 105 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 180 to 190°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 2150 | Prime PVC® | PVC, Rigid | Prime |
| Sup-tech S9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | ABS | Sup-tech |
| Vydyne® 47 NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Axiall PVC 9113 White 02 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Generic PVC+NBR | Generic | PVC+NBR | Generic |