VENYL SWGB300H
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EW4N54_VENYL-SWGB300H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SWGB300H is a 30% glass fibre/bead reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SWGB300H has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties, good surface finish and good compression strength. VENYL SWGB300H is available natural but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.1 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7100 | 4200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 5300 | 3450 | MPa | ISO 178 |
| Flexural Stress | 195 | 110 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 33 | 52 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 1905U0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Wellamid® GS25-66 22LH-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Fiberfil® PP-60/CC/40 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Eastar™ EN067, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Geon™ HTX Ultra LA436G | PolyOne Corporation | PVC Alloy | Geon™ HTX Ultra |