Hostaform® C 9021 GV1/20 XGM
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EV9ZzE_Hostaform-C-9021-GV1-20-XGM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GS2, 02-003, GF20 POM copolymer Injection molding type, reinforced with ca 20 % glass fibers; includes PTFE for improved wear performance; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage. Ranges of applications: For molded parts requiring improved low wear performance while exhibiting very high strength and rigidity as well as higher hardness. FMVSS = Federal Motor Vehicle Safety Standard (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 7400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.5 | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 210°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AFLAS® 150CS | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| Duron PA 6,6 10GF-IML | ProPolymers Inc. | Nylon 66 | Duron |
| Elastron® D D101.A63.N | Elastron USA, Inc. | SBS | Elastron® D |
| Karina PVC COMPOUND WHITE COLOR - E-800-10/1-A-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Monprene® RG-18250 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |