CERTENE™ LLHF-120C
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EUpxww_CERTENE-LLHF-120C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLHF-120C is a certified prime resin containing Hexene-comonomer designed for production of superior strength and low stiffness Blown films. LLHF-120C features easy processability and films exhibit high impact strength, very good tear and excellent creep resistances. LLHF-120C major applications include heavy duty bags, high strength liners, grocery bags and frozen food packaging. Maxim um recommended film drawdown is 0.5 mil. LLHF-120C contains medium slip and medium antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 230 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 260 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 57.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 41.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 630 | % | ASTM D882 |
| TD : Break, 25 µm | 880 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 350 | g | ASTM D1922 |
| TD : 25 µm | 8000 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 60 | ASTM D2457 | |
| Haze (25.4 µm) | 9.2 | % | ASTM D1003 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 215 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-300B | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| TIPPLEN® R 359 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| ALCOM® PC 740/4 RD1451-06LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| EnviroPCABS 5010IM | West Michigan Compounding | PC+ABS | EnviroPCABS |
| Delene 5580 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |