TECHNYL® C 216 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EUgPu2_TECHNYL-C-216-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced polyamide PA6, standard nucleation for fast cycling, for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.3 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2950 | 1100 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 85.0 | 45.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 100 | 270 | % | ISO 527-2/1A |
| Flexural Modulus | 2900 | 1000 | MPa | ISO 178 |
| Flexural Stress | 115 | 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | 84 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 4.5 | 75 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.40 | 3.90 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | -- | V | |
| Solution B | 575 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 225 to 235 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5132-75UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Titacon® EW901 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| EMOPLEN® AR 1205 RT2 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| TOTAL Polyethylene L 425 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |
| LNP™ LUBRICOMP™ RFL34 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |