Nylene® 4114-14 GL HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Custom Resins Group |
| Trademark: | Nylene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EThgxr_Nylene-4114-14-GL-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nylene® 4114-14 GL HS is a Polyamide 66 (Nylon 66) material filled with 14% glass fiber. It is available in North America for extrusion or injection molding. Important attributes of Nylene® 4114-14 GL HS are:
Typical application of Nylene® 4114-14 GL HS: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 78.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 12 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3450 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Melting Temperature | 259 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Shot Size | 25 to 75 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 260 to 293 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 282 to 310 | °C | |
| Nozzle Temperature | 279 to 307 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Injection Pressure | 34.5 to 103 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 27.6 to 82.7 | MPa | |
| Back Pressure | 0.00 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V75W | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| SABIC® HDPE B5202 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Flontech® FT-1-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hostacom ERC 475L NAT | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRICOMP™ ECL36 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |