Latiohm 57-05 PD01 G/15
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiohm |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ESRDGf_Latiohm5705PD01G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Semiconductive/dissipative product based on Semi-aromatic polyammide (PPA). Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Transverse flow : 2.00mm | 0.75 - 1.1 | % | ISO 294-4 |
| Flow : 2.00mm | 0.35 - 0.65 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 13500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 270 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBIT® 1500A15 | Samyang Corporation | PBT | TRIBIT® |
| Diamond ABS VP33 Black 1402 | Network Polymers, Inc. | ABS | Diamond ABS |
| KumhoSunny PC 2500FR | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| IPC PP 4820H-T | International Polymers Corporation | PP Homopolymer | IPC PP |
| Hostacom TRC 787N E C11323 | LyondellBasell Industries | PP Copolymer | Hostacom |