Hanwha Total PE F120A
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EQk75w_Hanwha-Total-PE-F120A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F120A is a high-density polyethylene resin for films. This grade is designed to be processed in conventional blown film equipment. F120A is suited to general-purpose packaging films and shopping bag applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.044 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.6 | MPa | ASTM D638 |
| Fracture | 29.4 | MPa | ASTM D638 |
| Apparent Bending Modulus | 981 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 53.9 | MPa | ASTM D882 |
| TD : Break, 20 µm | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 380 | % | ASTM D882 |
| TD : Break, 20 µm | 450 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 200 | g | ASTM D1709 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 290 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 1 |
| Additional Information |
|---|
| Elmendorf Tear Strength MD, ASTM D785: 6 kg force/cm²Elmendorf Tear Strength TD, ASTM D785: 200 kg force/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 190 | °C | |
| Cylinder Zone 2 Temp. | 160 - 190 | °C | |
| Cylinder Zone 3 Temp. | 160 - 190 | °C | |
| Cylinder Zone 4 Temp. | 160 - 190 | °C | |
| Cylinder Zone 5 Temp. | 160 - 190 | °C | |
| Die Temperature | 180 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 3 to 6Frost Line Height: 40 to 120 cm |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2001-50A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| ALTECH® ABS A 1000/100 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| Five Plus™ HPP10C | Noble Polymers | PP Homopolymer | Five Plus™ |
| Sarlink® TPE EE-2260B (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| LEXAN™ HFD4271 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |