Hostalen CRP 100 black
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EQUck9_Hostalen-CRP-100-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen CRP 100 black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 6.4 | g/10 min | |
| 190°C/5.0 kg | 0.23 | g/10 min | |
| FNCT (80°C) 1 | > 1.4 | month | ISO 16770 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus 2 | DIN 19537-2 | ||
| 1 min | 1.20 | GPa | |
| 2000 hr | 0.330 | GPa | |
| 24 hr | 0.560 | GPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Elongation - TD | > 350 | % | EN 638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 30 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO TR 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Tensile Creep Modulus 3 | ISO 899-1 | ||
| 1 hr | 850 | MPa | |
| 1000 hr | 360 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 26 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 200 to 280 | °C | |
| Middle Temperature | 200 to 280 | °C | |
| Front Temperature | 200 to 280 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 4.0 MPa, 2% Arkopal N 100 |
| 2 . | 4 point loading method |
| 3 . | 2.0 MPa load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC GSK 6515 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Iupilon® GPN2030DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| PALRAN® R S 10 | pal plast GmbH | ABS | PALRAN® |
| POLIMAXX 2564PCXTA6 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| MAXAMID™ EPDMRC036-HSL-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |