EL-Lene™ LD1902F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EOG8k1_EL-Lene-LD1902F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-LENE LD1902F is a LDPE resin with Slip and Antiblocking agent. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 38 µm | 245 | MPa | |
| 2% Secant, TD : 38 µm | 275 | MPa | |
| Tensile Strength | ASTM D882 | ||
| TD : Yield, 38 µm | 11.8 | MPa | |
| MD : Break, 38 µm | 22.6 | MPa | |
| TD : Break, 38 µm | 18.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 260 | % | |
| TD : Break, 38 µm | 720 | % | |
| Dart Drop Impact (38 µm) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 370 | g | |
| TD : 38 µm | 100 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Melting Temperature | 110 | °C | ASTM D2117 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (38.0 µm) | 50 | ASTM D2457 | |
| Haze (38.0 µm) | 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 to 170 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 3962 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Cheng Yu N6C1 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| ExxonMobil™ PP1074KNE1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Hostacom PPR 1042 101070 | LyondellBasell Industries | PP Copolymer | Hostacom |
| ESTOPLAST XU 6230BB11 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |