Jamplast Ex-17 ABS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EO5y1t_Jamplast-Ex-17-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jamplast Ex-17 ABS is a medium-gloss, High-impact extrusion grade of ABS (acrylonitrile butadiene styrene). It provides a good balance between ridity and impact strength, and has a stiff melt flow suitable for extrusion and thermoforming. Jamplast Ex-17 ABS is easy to color with ABS color concentrates. This resin is designed for either profile extrusion or substrate coextrusion. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 40.0 | MPa | ASTM D638 |
| Flexural Modulus (3.17 mm) | 1930 | MPa | ASTM D790 |
| Flexural Strength (3.17 mm) | 57.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.0 | °C | ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 68.9 to 82.7 | MPa | |
| Back Pressure | 0.689 to 1.38 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 3.2 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y180L (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Nipol® 1051 | Zeon Chemicals L.P. | NBR | Nipol® |
| DynaMix™ XP-5531 | Polymer Dynamix | TP, Unspecified | DynaMix™ |
| EMOPLEN® A 2540 T1 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Sylvin 9980-65 Red 683 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |