THERMOLAST® K TC7UVZ (Series: UV/AP)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | KRAIBURG TPE |
| Trademark: | THERMOLAST® K |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ENxqUq_THERMOLAST-K-TC7UVZ-Series-UV-AP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The UV/AP Series is your material solution for applications requiring high UV resistance. It is particularly suited for automotive exterior components. The compounds comply with GM standard GMW 16233. Typical applications
Material advantages
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 70 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 6.20 | MPa | ISO 37 |
| Tensile Elongation 2(Break) | 600 | % | ISO 37 |
| Tear Strength 3 | 26 | kN/m | ISO 34-1 |
| Compression Set 4 | ISO 815 | ||
| 23°C, 72 hr | 24 | % | |
| 70°C, 24 hr | 59 | % | |
| 100°C, 24 hr | 74 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 25.0 to 40.0 | °C | |
| Injection Pressure | 20.0 to 100 | MPa | |
| Back Pressure | 2.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Type S2, 200 mm/min |
| 2 . | Type S2, 200 mm/min |
| 3 . | Method Bb, Angle (Nicked) |
| 4 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 36 G 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Tenac™ LT805 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| VITAMIDE® AR13 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| Wellamid® MR409 22H-NBK4 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| EPAMOULD 665A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |