Desmopan® 445
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ENXWZt_Desmopan-445.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; grease and oil-resistant; good heat resistance; low compression set; Application; Automotive engineering; Injection molded engineering parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1220 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 93 | ||
| Shore D, 15 sec | 44 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 56.4 | MPa | |
| 10% Strain, 23°C | 5.50 | MPa | |
| 50% Strain, 23°C | 11.6 | MPa | |
| 100% Strain, 23°C | 14.3 | MPa | |
| 300% Strain, 23°C | 31.5 | MPa | |
| Tensile Strain 4(Break, 23°C) | 490 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 25.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 790 | MPa | |
| 20°C | 103 | MPa | |
| 60°C | 58.0 | MPa | |
| Torsional Storage Modulus | ISO 6721-2 | ||
| -20°C | 280 | MPa | |
| 23°C | 25.0 | MPa | |
| 70°C | 16.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 35 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5(23°C) | 95 | kN/m | ISO 34-1 |
| Compression Set (70°C, 24 hr) | 35 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 210 to 235 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-FR2A-D | Polymer Resources Ltd. | PC | PRL |
| WINTEC™ WMX03 | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| DAI-EL™ G-671 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| KumhoSunny PC/AES HEC0245 | Shanghai KumhoSunny Plastics Co., Ltd. | AES+PC | KumhoSunny PC/AES |
| TOTAL Polypropylene PPH 3485WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |