LNP™ LUBRICOMP™ ML004LS compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EMgNg5_LNP-LUBRICOMP-ML004LS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized, Low Extractible. Also known as: LNP* LUBRICOMP* Compound ML-4040 HS LE Product reorder name: ML004LS |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1920 | MPa | ASTM D638 |
| -- | 1670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 33.4 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2/5 |
| Break 3 | 16.7 | MPa | ASTM D638 |
| Break | 22.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 5.7 | % | ISO 527-2/5 |
| Break 5 | 38 | % | ASTM D638 |
| Break | 28 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1720 | MPa | ASTM D790 |
| -- 7 | 1480 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.28 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.100 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 7.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256 |
| 23°C 8 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 9 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.80 | J | ASTM D3763 |
| -- | 2.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 116 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 93.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 56.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.5E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.4E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ OM 6059-9 | PolyOne Corporation | TPE | Versaflex™ |
| NYLOY® MG-0023N-V0 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Fainplast PVC KL 96/5 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Epiall® 1908M-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Epiall® |
| OPTODYNE™ UV-2100 | DAIKIN AMERICA, INC. | Epoxy | OPTODYNE™ |